TechnicalData
AQUA LEAF
WATER BASED METALLIC LOOK FINISH - (with UV protection)
Aqua LeaflM is a water based,lead free,non-gassing, metallic-like finish coatingwith
DESCRIPTION:
built in ultraviolet protection. It is formulated with nacreouspigments to yield a lustrous
metallic look. It dries to a flexible, weather and fade resistant,bright metallic like finish
and exhibits excellent adhesionto wood, metal, treated and untreatedvinyl and many
other substrates.Non-Flammable, non-toxic when cured, low odor.
Aqua LeaflM can be usedon any properly primed white interior or exterior substrate,
RECOMMENDED
vinyl, plastic and glass. Used by
such as,wood, plaster,wallboard,steel,canvas,
US E S :
furniture and cabinet refinishers for a variety ofdecorative applications. Used
extensively by specialty painters and artists for faux finishes and glazing.
must be cleanand free from looseor peelingpaint, grease, oil, dirt, rust,
SURFACE All surfaces
miil scaleand other contaminants.If this procedure is not observed,the drying and
PREPARATION:
adhesionofany coatingwill be adverselyaffected.
Previously Painted Surfaces: Dull glossyareasby light sandingto enhanceadhesion.
Prime with Prime-All. PaintedMetal Surfaces Ronan Prime Lock DTM Primer.
use
Wood Surfaces: Cleansuffaceto eliminateoil, grease and other contaminants.Prime
with Ronan Sticktite White Primer or Prime-All.
Ferrous Metal Surfaces: Removelooserust and scalewith wire brush, steelwool
All oil, greaseand contamination must be removed. Acidic or alkaline
and/or sandpaper.
surfacesshould be neutralized. Prime with Ronan Galvanized Primer, White Universal
Primer or Prime Lock DTM Primer.
Galvanized Metal and Aluminum: Surfaceshouldbe wiped with xylene or ketoneto
remove oil and grease.A mild solutionof phosphoricacid shouldbe used for etchingto
assure good bond. If acidsare not availableslight surfacesandingwill be beneficial.
a
Prime with Ronan White UniversalPrimer or Prime Lock DTM Primer. For more
complete information on preparationand priming galvanizedmetal and aluminum refer
Sheet#SSGA.
to Ronan Substrate
Concrete Surfaces: A white powdery deposit(efflorescence), found on concreteand
masonry surfacesshould be completely removed with a stiff wire brush. New concrete
shouldbe etchedwith a
should set4 - 6 weeksbefore coating. All concretesurfaces
solution of 4 parts water to I part muriatic acid. Let solution soak on surface for I 5
minutes before rinsing with clear water. Allow 48 hours to dry before painting. Prime
with Prime-All (2 coats).
MDO Plywood: Clean surfaceto eiiminate oii, greaseand other contaminants. Prime
face with Prime-All or MDO Primer. All edgesshould be puttied and then primed with
two coatsof RonanPrime-All or MDO Primer.
Masonite: Cleansurfaceto eliminateoil, and contaminants.Prime with Prime-All.
Vinyl Surfaces: Pretreat wiping with isopropyl alcohol to help lower surfacetension,
by
let dry. Prime with Ronan Metro Vinyl Primer, Prime-All or Vinyl Cote Flat.
PVC and Plastic Surfaces: Pretreat wiping with isopropyl alcohol to help lower
by
surfacetension,let dry. Prime with RonanPrime Lock DTM Primer.
Follow surfacepreparation instructions. Stir thoroughly. Apply by brush, roller or spray.
APPLICATION:
Brush: Any good quality synthetic bristle brush.
Roller: A shortnap (3/8 inch or less)industrialroller will give the best results.
Spray: For sprayingbegin by slowly adding 1 pint Flow Control to I gallon of Aqua
(maximum I ll2 pint Flow Control to
LeafrM. Mix well. Slowly add more if necessary
I gallon of Aqua LeaflM). Apply severalmist coatsfor coverageand film build. Dry
Time betweenmist coats:@70" F;50% RelativeHumidity - t hour.
SPRAY GUNS: The following equipmenthas beenusedsuccessfully combination in
with Aqua LeaflM and Aqua LeaflM Flow Control. I - Graco SpecialPressure Assist
with specialtip.2 - GracoPressure with specialtip.
Pot
|