High Performance 100% Solids Epoxy
Chemical & Solvent Spill Resistance
Product Technical Data
Technical Data Std Colors Custom Colors Reagent 24 Hours 1 Week
Generic Type Cycloaliphatic Amine cured epoxy Brake Fluid Excellent Fair
Ethylene Glycol (Anti-Freeze) Excellent Excellent
Pigment Type TiO2 & inerts Varies by color
Unleaded Gasoline Excellent Good
Volume Solids (mixed) 100% 100%
Diesel Fuel Excellent Excellent
Theoretical Coverage At 10 Mils 160 sq. ft./gal 160 sq. ft./gal
37% Sulfuric Acid (Battery Acid) Excellent Fair
Film Thickness 鈥? Wet 8 鈥? 12 Mils 8 鈥? 12 Mils
Motor Oil (SAE30) Excellent Excellent
鈥? Dry 8 鈥? 12 Mils 8 鈥? 12 Mils
Hydraulic Fluid Excellent Excellent
Dry Time @ 70掳 F 鈥? To Touch 8 Hours 8 Hours
10% Acetic Acid Very Good Fair
鈥? To Recoat 16 Hours 16 Hours
30% Hydrochloric Acid (Muriatic) Excellent Good
Dries By Chemical Cure Chemical Cure
Toluene Good Fair
Dry Heat Resistance 300掳 F 300掳 F
Xylene Very Good Fair
Viscosity @ 70掳 F (mixed) 90 KU 85 KU
Mineral Spirits Excellent Excellent
Flash Point (Seta) > 203 掳F > 203 掳F
Methanol Fair Poor
60掳 Specular Gloss 85% Minimum 85% Minimum
Ethanol Good Fair
Surface Temperature 鈥? Min. 50掳 F 50掳 F
50% Sodium Hydroxide Excellent Excellent
at application 鈥? Max. 85掳 F 85掳 F
Methyl Ethyl Ketone (MEK) Fair Poor
Surface must be dry and at least 5掳 above the dew point
Reducer (Thin ONLY for critical application situations) xylol xylol Jet Fuel - JP4 Excellent Excellent
Reduction 鈥? Brush 5% 5% Deionized Water Excellent Excellent
(Reduction will slow set 鈥? Roller 5% 5%
Fully cured epoxy castings of 1/8" thickness were immersed in listed reagents for
time of material ) 鈥? Spray not recommended not recommended
24 hours. Samples were then removed, weighed, and hardness tested immediately.
Clean Up Thinner Magnet S8 Reducer or xylol
Explanation of results: Ratings are based on the samples resistance to
Mixing Ratio (by volume) 1:1 1:1
degradation by the reagent solution. Damage caused by solvent or chemical spills
Mixing Time 3 Min. 3 Min.
will soften and swell epoxy coatings. Resistance to damage is determined by a
Working Pot Life @ 70掳 F 60 Minutes 60 Minutes
coatings ability to remain hard with no swelling or absorption of the reagent.
Induction time none following 3 minute mixing
Castings completely unaffected by reagents scored a result of excellent. Castings
Weight Per Gallon (mixed) 10.9 lbs 10.2 lbs
marginally affected by reagents but returned to normal hardness after removal from
Storage Temperature 鈥? Min. 50掳 F 50掳 F
reagent scored results of very good. Castings suffering slight damage and a small
鈥? Max. 80掳 F 80掳 F
weight gain scored a result of good. Castings with ratings of fair suffered permanent
Volatile Organic Compounds (VOC) damage and weight loss indicating that the reagent was dissolving the sample.
Mixed, Unthinned Grams/Liter zero zero Samples were cured for 7 days at 77潞F before testing.
Lbs./Gal. zero zero
Physical Properties Data The study above shows that MAGNATILE鈩? provides very
good to excellent chemical resistance when exposed to a
Test Test Method Results variety of common solvents, acids and bases.
For floors subject to frequent heavy abuse such as
Compressive Strength ASTM C-579 14,850 psi
automotive repair shops and body shops, the use of an
Flexural Strength ASTM C-580 8390 psi
engineered chemical resistant topcoat may be necessary
Elongation ASTM C-638 0.40%
to achieve greater resistance to abrasions and frequent
Tensile Strength ASTM C-307 9,200 psi
chemical spills.
Hardness ASTM D-2240 84
Ask about MAGNATILE鈩? Chemical Resistant Urethane
Bond Strength ASTM D-4541 530 psi
Clear Coat and upgrade your floor with the required
Water Absorption ASTM C-413 0.15%
protection for these situations.
Coefficient of Friction ASTM D-2047 0.6
Flammability ASTM D-635 self-extinguishing
Abrasion Resistance
MAGNET PAINT & SHELLAC CO., INC.
(Taber test) ASTM D-4060 0.06 g
336 Bayview Avenue, Amityville, NY 11701
Impact Resistance ASTM D-2794 > 60 in-lbs
(631) 842-7700 Fax (631) 842-8222 Toll Free 1-800-922-9981 Email: info@magnetpaints.com
Heat Resistance 140掳 F (60掳 C)
www.magnetpaints.com
Note: All tests run in triplicate. Above values are the average results.
Epoxy
100%
Solids
|